YT4500-P1 integrated dual-purpose coating thickness gauge Introduction
The YT4500-P1 integrated dual-purpose coating thickness gauge provides fast, accurate non-destructive testing of the thickness of various coatings applied to metal substrates. The instrument is fully compliant with the magnetic and eddy current test principles specified in ISO 2178, ISO 2360, GB/T 4956, GB/T 4957, ASTM B499, etc. The instrument is stable, accurate and powerful, and is widely used in manufacturing and metal. The field of surface engineering testing, such as processing industry and chemical industry, is the basic equipment of coating surface treatment industry.
Fe-based probes measure the thickness of various non-magnetic coatings applied to various magnetic substrates such as steel, such as iron paint layers, dust coats, ceramic coatings, chrome plating, copper plating, and galvanized coatings. Wait.
The NFe-based probe detects the thickness of all insulating coatings applied to non-magnetic metal substrates (such as aluminum, copper, brass, stainless steel, etc.), such as paint layers, dusting layers, and ceramic coatings. Features
1. It can quickly and accurately test the thickness of coatings of various magnetic metal substrates (magnetic method) and non-magnetic metal substrates (eddy current method);
2. One-handed design, perfect combination of human mechanics structure design;
3. It can quickly and automatically identify the iron matrix and the non-ferrous matrix, one-button test;
4. The instrument can be accurately calibrated by single point calibration and multi-point calibration;
5. Low power consumption, more power saving, low battery alarm;
6. With backlit display, buzzer prompts;
7. High wear-resistant probe, no less than 800,000 measurements;
8. Multiple measurement modes: single point measurement, continuous measurement; Technical Parameters
Product model: YT4500-P1
Product Name: One-purpose dual-use coating thickness gauge
Meet the standards: ASTM B499, ASTM D1400;
ISO 2178, ISO 2360, ISO 2808;
GB/T 4956/4957, JB/T 8393
Base: Fe/NFe
Probe form: integrated
Resolution: 0.1/1μm
Measuring range: 0~1250μm
Measurement accuracy: Zero point correction: ± (3% H + 1) μm;
Two-point correction: ± (1 ~ 3% H + 1.5) μm;
Note: H is the sample thickness
Minimum measurement size: Magnetic: 10 × 10mm;
Non-magnetic: 10×10mm
Minimum measured thickness: Magnetic: 0.2mm;
Non-magnetic: 0.05mm
Minimum curvature: convex radius 5mm; concave radius 10mm
Display unit: μm
Power: 2 AA batteries (AA alkaline batteries or Ni-MH rechargeable batteries);
Size: 102 × 66 × 24mm
Weight: 99g (with battery)
Quality Software: /
Working temperature: 0~40oC (10~90% RH without condensation)
Storage temperature: -10~50oC
Standard accessories: 2 bases (iron base, aluminum base), wrist strap, calibration test piece
Optional accessories: Calibration test piece (12μm, 25μm)
Note: The technical parameters are for reference only, subject to the actual sales of the product.
Introduction
The YT4500-P1 integrated dual-purpose coating thickness gauge provides fast, accurate non-destructive testing of the thickness of various coatings applied to metal substrates. The instrument is fully compliant with the magnetic and eddy current test principles specified in ISO 2178, ISO 2360, GB/T 4956, GB/T 4957, ASTM B499, etc. The instrument is stable, accurate and powerful, and is widely used in manufacturing and metal. The field of surface engineering testing, such as processing industry and chemical industry, is the basic equipment of coating surface treatment industry.
Fe-based probes measure the thickness of various non-magnetic coatings applied to various magnetic substrates such as steel, such as iron paint layers, dust coats, ceramic coatings, chrome plating, copper plating, and galvanized coatings. Wait.
The NFe-based probe detects the thickness of all insulating coatings applied to non-magnetic metal substrates (such as aluminum, copper, brass, stainless steel, etc.), such as paint layers, dusting layers, and ceramic coatings.