LC-TS5-type furnace front hot metal composition analyzer Introduction:
LC-TS5-type front hot metal composition analyzer is a new generation of frontal hot metal management instrument with stable performance and high measurement precision produced by our company. It realizes fast and accurate real-time analysis of the temperature curve of molten iron in the sample cup with time To capture a large amount of information on the thermal effect of hot metal coagulation. Through a series of complicated data processing, the carbon content, silicon content, carbon equivalent, tensile strength, primary crystallization temperature and eutectic temperature in molten iron can be quickly and accurately determined.
The difference between thermal analyzer and spectrochemical analysis is that the thermal analyzer measures the formation of cast iron structure and is a comprehensive result of the effect of different contents of all the elements in the molten iron on the formation of cast iron. The effective equivalent content in the molten iron is detected.
In order to accurately measure the convergence of each element in the molten iron to measure the specific content of each element of the molten iron, the role of each element on the formation of cast iron organization the role of direction, these work in the furnace before the time waiting for hot metal It is impossible to complete. Even if possible, it is not possible to adjust the content of each element to the specified range.
However, the thermal analyzer can directly measure the comprehensive effect of different contents of all elements on the formation of cast iron structure, and directly adjust the comprehensive effect result to realize the expected cast iron structure. This is the biggest advantage of the thermal analyzer compared with other detection methods, and also in developed countries Casting is widely used reasons.
LC-TS5-type hot metal detector before the test time is about 2 minutes, the hot metal can wait for the time to complete the test, and then calculated automatically based on the carburizing agent, ferrosilicon, scrap cast iron composition to be adjusted to get After the appropriate hot metal ingredients for casting. Features:
1. Complete industrial environment design, desktop structure, stable and reliable performance, easy to operate.
2. The target material selection (FC, FCD): up to 10 commonly used materials can be set.
3. For the rapid determination of the furnace before the determination of the original iron cast iron water carbon CE%, carbon content C%, silicon content Si%, tensile strength (FC) inferred value.
4. Measuring range: C%: 2.8% -4.2%, Si%: 0.9% -3.0%, CE%: 3.2% -4.83%.
5. Measurement accuracy, good stability. C% accuracy within 0.05%, Si% accuracy within 0.1%.
6. Measurement speed, measurement time does not exceed 3 minutes, easy to adjust ingredients before the stove.
7. Carbon, silicon compensation correction: According to the chemical analysis or spectrometer data can be adjusted to compensate silicon carbon value.
8. Cooling curve and measurement data CE, C%, Si%, TL, TE simultaneously displayed, clear and intuitive.
9. When the measured value is not within the upper and lower limit of the target value, a flashing up / down arrow will appear.
10. According to the determination of the composition of the ingredients, has set the amount of molten iron, the target composition and material retention rate automatically calculate the amount of material deficiency, easy to adjust the furnace quickly carbonation agent, ferrosilicon, scrap addition, so that C%, Si% Enter the target upper and lower limits.
11. Can be set at the same time 10 calibration lines to adapt to different types of applications.
12. Has a wealth of input / output and communication capabilities, can communicate with the computer.
13. Automatic print options: with any one printer, print curves and measurement data quickly. Technical Parameters:
1. Carbon content C% of the test: measurement range of 2.8 to 4.2%, measurement accuracy ≤ ± 0.05
2. Silicon content SI% of the test: measurement range of 0.9 to 3.0%, measurement accuracy ≤ ± 0.1
3. Carbon equivalent CE% detection: measurement range of 3.2 to 4.8%, measurement accuracy ≤ ± 0.1
4. visually shows the cooling curve on the screen.
5. Can be any formula for calibration line call.
6. Can be set ten calibration curve, to meet the different materials in the carbon content of silicon measurement.
7. According to the material requirements and measurement results automatically calculate the feeding amount.
8 can be set temperature compensation.
Introduction:
LC-TS5-type front hot metal composition analyzer is a new generation of frontal hot metal management instrument with stable performance and high measurement precision produced by our company. It realizes fast and accurate real-time analysis of the temperature curve of molten iron in the sample cup with time To capture a large amount of information on the thermal effect of hot metal coagulation. Through a series of complicated data processing, the carbon content, silicon content, carbon equivalent, tensile strength, primary crystallization temperature and eutectic temperature in molten iron can be quickly and accurately determined.
The difference between thermal analyzer and spectrochemical analysis is that the thermal analyzer measures the formation of cast iron structure and is a comprehensive result of the effect of different contents of all the elements in the molten iron on the formation of cast iron. The effective equivalent content in the molten iron is detected.
In order to accurately measure the convergence of each element in the molten iron to measure the specific content of each element of the molten iron, the role of each element on the formation of cast iron organization the role of direction, these work in the furnace before the time waiting for hot metal It is impossible to complete. Even if possible, it is not possible to adjust the content of each element to the specified range.
However, the thermal analyzer can directly measure the comprehensive effect of different contents of all elements on the formation of cast iron structure, and directly adjust the comprehensive effect result to realize the expected cast iron structure. This is the biggest advantage of the thermal analyzer compared with other detection methods, and also in developed countries Casting is widely used reasons.
LC-TS5-type hot metal detector before the test time is about 2 minutes, the hot metal can wait for the time to complete the test, and then calculated automatically based on the carburizing agent, ferrosilicon, scrap cast iron composition to be adjusted to get After the appropriate hot metal ingredients for casting.