JB - TS3 molten silicon carbon analyzer Brief introduction:
Before the product is also called the furnace hot metal composition analyzer, it is widely used in field measurement of gray iron, iron, ductile iron and vermicular iron and low alloy cast iron, such as the original molten iron, carbon equivalent and carbon content, pouring temperature, silicon content TM, TL the liquidus temperature, solidus temperature, TS and other key indicators. Features:
1. The measured results display direct reading, measuring time for 2-3 minutes, is advantageous for the casting engineer ingredients at the scene.
2. The equipment operation is simple, free maintenance, general furnace Labour can use at the site.
3. The instrument is portable, can be free to move on the mantelpiece, furnace can be used at the same time, a new instrument.
4. Put an end to the product quality accidents, reduce the waste and recycled, reduce the production cost.
5. The instrument can measure before or after inoculation of molten iron.
6. The instrument can automatically control the important metallurgical parameters. It for gray cast iron solidification automatic measurement, was relieved from the manual operation. Can connect large remote displays, lights, computer, printer. Technical parameters:
Measurement parameters: 1. The contents of carbon, silicon, carbon equivalent CEL, super-cooling degree delta T, the greater degree of cold delta TM Rm, tensile strength, hardness HB, quality coefficient R/H, the cluster number MEG, graphitization factor K, pouring temperature TM, TL the liquidus temperature, solidus temperature, TS.
2. The measuring range: according to ICEC584, type K (Nicr - Ni) 200 ℃ to 1370 ℃ C: 2.1 4.2% Si: 0-20% CEL: 2.5 to 5.0
3. Precision: < + ℃ for CET plus or minus 0.047% C + / - 0.04% Si + / - 0.1%
4. Display: four LED display number 560 mm resolution: 1 ℃
5. Mode of operation: the nine keys to choose the required parameters, according to the "Auto" button is cycle. Carbon, silicon, can be adjusted through the panel knob precision.
6. The output method: 4-20 ma
7. Installation dimensions: length: 380 mm width: 290 mm height: 120 mm
Brief introduction:
Before the product is also called the furnace hot metal composition analyzer, it is widely used in field measurement of gray iron, iron, ductile iron and vermicular iron and low alloy cast iron, such as the original molten iron, carbon equivalent and carbon content, pouring temperature, silicon content TM, TL the liquidus temperature, solidus temperature, TS and other key indicators.